SAITRON HF 600 WH
Description:
SAITRON HF 600 WH is a basic coated low heat input “Anti-Wear” Mn-Cr-Ni-Mo alloyed work-hardening type hardfacing electrode. Excellent choice for surfacing and building-up worn out parts of mining equipments, earthmoving equipments, railway point and crossing and components made of manganese. Also used for joining on manganese casting to mild steel and other carbon steels. Weld deposit structure is austenitic, which is tough and easily work-hardened under impact condition, ultimately increasing the abrasion resistance.
Applications:
Used for surfacing in Cement plants, Mining equipments, Earthmoving equipments, etc. It is highly suitable for welding 13% Mn steel, rail point and crossing, rollers, mill hammers, Shovel, Dredge buckets, heavy crushing equipments like jaw crusher, Gyratory crusher cones, Swing hammers, Excavator teeth, crusher mantles and shredder hammers, hard surfacing of hot shear, rings in rotary furnace, forging moulds, hot forging dies etc. Used for overlaying, cushioning and building up of low, medium carbon, low alloy and Hadfield steels. Deposits are extremely tough and resist deformation under repeated impact loads.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Maintain short arc and chip slag between passes. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. Preheat is usually not necessary unless very heavy sections are involved. No preheat should be used on manganese steel. Do not allow manganese steel interpass temperature above 2500 C..
Typical Mechanical Properties of Weld Metal
| Hardness (As Deposited) | Hardness (Work Hardened) |
| 250 BHN max. | 500 BHN max. |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 90-120 | 125-150 | 150-190 |
SAITRON HF 635
Description:
SAITRON HF 635 is low heat input “Anti-Wear” Cr-Mo alloyed steel electrode. It is used for high build-up as cushioning layers before hardfacing with harder abrasion-resistant weld alloys. Weld deposits is tough and machinable with high compressive strength. Resist severe impact condition when used on Low and Medium carbon steels, Low & Medium alloy steels. High resistance to rolling and sliding friction. Easy welding with self removal slag. Weld deposit is dense and crack free.
Applications:
Used on Slideways, Guides and couplings, wheel crowns, Shafts and wheels, Sprockets, carrier and track rollers, idlers of earth moving equipments, crane wheels, pinions and gears, tail bars, wobbler ends of rolls and couplers in steel plants and sugar mills, girth gears of cement mills and power stations and supporting rollers of kiln tyres. Important applications are gear teeth, rail-ends and crossing, shaft, mill guide plates, pulley, Rope winches, Brake drums, clutches, wheel, axles, couplings, sprockets, pinion etc.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC + at the lowest amps. Maintain short arc and chip slag between passes. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. Preheat is usually not necessary unless very heavy sections are involved.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | Hardness (Flame Hardened) |
| 270 – 350 BHN | 340 – 375 BHN |
| Diameter (mm) | 2.50 | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 50-85 | 85-115 | 125-150 | 150-190 |
SAITRON HF 655
Description:
SAITRON HF 655 is a low heat input “Anti-Wear” Cr-Mo-V alloyed all position hardfacing electrode. Weld deposit is of carbide type and have good abrasion resistance. In as welded condition it gives high hardness which is suitable for soil abrasion and light impact abrasion. Machining is possible by grinding only.
Applications:
It is suitable for mining and earthmoving equipments, bull dozers blades, tractor parts, Shear blades, Plow shares, bucket teeth, pug mill crusher, coal chutes, dipper teeth, screw conveyers, crusher plates, brick machinery, pellet plant parts and tamping tools. This alloy can be used on components of Steels, Manganese steels etc.
Note on Usage:
Rebake the electrodes at 300°C for 1 hour and keep it at 100°C prior to use to prevent blowholes in the weld deposit Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Maintain short arc and chip slag between passes. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. Preheat is usually not necessary unless very heavy sections are involved. Base material of high carbon steels should be preheated to 2000C to 3000C, depending on their composition and thickness of the job. No preheat should be used on manganese steel. On highly crack sensitive jobs and Manganese steel jobs buffer layer of SAITRON 214 or SAITRON HF 600 WH electrode is recommended.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 55 – 60 HRC |
| Diameter (mm) | 2.50 | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 50-85 | 85-120 | 125-150 | 150-190 |
SAITRON HF 660
Description:
SAITRON HF 660 is a low heat Chromium Carbide anti-wear alloy offer excellent resistance against abrasion, pressure and mild to medium impact on steel components of low alloy and manganese steels. Easy welding with self slag removal. Bright weld bead with smooth appearance. Stable arc. High recovery.
Applications:
It is suitable for Sugar Cane Knives, Bull dozer blades, Crusher teeth, Pump bodies, Dredging pump impellers, Mixer blades, Scraper blades, Pulleys, Ripper teeth, Crushing & Pulversing plants, Coal burner pipes, Coal nozzles, Fibrizer/Mincer hammers, Rolling mill entry & exit guides etc.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. High carbon steel base metal to be preheated to 2500C. For higher build up on carbon or high alloy steels use SAITRON 223/230 as a cushioning layer. For manganese steels, restrict heat build up to 1500C and use SAITRON 205 / SAITRON HF 600 WH alloy if necessary as a cushion layer. No preheat should be used on manganese steel.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 57 – 62 HRC |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 95-125 | 135-175 | 160-200 |
SAITRON HF 661
Description:
SAITRON HF 661 is a low heat input “Anti-Wear” C-Cr-Mo and special alloyed all position hardfacing electrode. Weld deposit is of special carbide type and have good abrasion resistance. In as welded condition it gives high hardness above 60 HRC which is suitable for soil abrasion and medium impact abrasion. Machining is possible by grinding only.
Applications:
It is suitable for mining and earthmoving equipments, bull dozers blades, tractor parts, Shear blades, Plow shares, bucket teeth, pug mill crusher, coal chutes, dipper teeth, screw conveyers, crusher plates, brick machinery, pellet plant parts and tamping tools. This alloy can be used on components of Steels, Manganese steels etc.
Note on Usage:
Rebake the electrodes at 300°C for 1 hour and keep it at 100°C prior to use to prevent blowholes in the weld deposit. Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Maintain short arc and chip slag between passes. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. Preheat is usually not necessary unless very heavy sections are involved. Base material of high carbon steels should be preheated to 200°C to 300°C, depending on their composition and thickness of the job. No preheat should be used on manganese steel. On highly crack sensitive jobs and Manganese steel jobs buffer layer of SAITRON 214 alloy or SAITRON HF 600 WH electrode is recommended.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 60 – 64 HRC (Single Layer on mild steel) |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 90-120 | 120-150 | 150-190 |
SAITRON HF 662
Description:
SAITRON HF 662 is a C-Cr-W alloyed hardfacing low heat electrode. Special alloy addition gives microstructure of complex carbide, so that the weld deposit has high abrasion resistance with mild impact even at high temperature upto 4500C. Smooth and stable arc. The weld metal achieves the hardness upto 65 HRC with three layers deposit.
Applications:
It is suitable for hardfacing the components which are subject to abrasion, impact and compressive loads, used in Cement industry, Steel Industry, Power plants, etc. Parts like Hammers, Buckets teeth, Blowbars, Dredger pumps parts, Earthmoving parts, etc.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. High carbon steel base metal to be preheated to 2500C. For higher build up on carbon or high alloy steels use SAITRON 223/230 as a cushioning layer. For manganese steels, restrict heat build up to 1500C and use SAITRON 205 / SAITRON HF 600 WH alloy if necessary as a cushion layer. No preheat should be used on manganese steel.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 62 – 66 HRC (Third Layer on mild steel) |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 95-125 | 130-160 | 160-200 |
SAITRON HF 663
Description:
SAITRON HF 663 is a highly alloyed with C-Cr-Mo-V hardfacing electrode. Special alloy addition gives microstructure of primary chromium carbide and complex carbide of Mo & V, so that the weld deposit can sustain severe abrasion and erosion resistance even at high temperature upto 6000C. It can also be used on equipments operating in corrosive environments. Smooth and stable arc. Very High recovery with less slag.
Applications:
It is suitable for Coal burner pipes, Coal nozzles, Fibrizer/Mincer hammers, Sinter breaker arms, steel mills and sinter plants, Crusher sieves, Hot Slag Conveyors, Clinker Conveyor chains, Augers, Slurry pumps, Billet Conveyor Guides, dust exhausters, Coke pusher shoes, vertical Coal mill rollers, Dredger components and Tip casting etc. Also in earth moving machines, mixers, mineral dressing equipments, especially where live coal and slag are treated. SAITRON HF 663 is useful in power plants, steel plants and cement plants etc.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. High carbon steel base metal to be preheated to 2500C. For higher build up on carbon or high alloy steels use SAITRON 223/230 as a cushioning layer. For manganese steels, restrict heat build up to 1500C and use SAITRON 205 / SAITRON HF 600 WH alloy if necessary as a cushion layer. No preheat should be used on manganese steel.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 60 – 65 HRC |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 95-125 | 130-165 | 160-200 |
SAITRON HF 665
Description:
SAITRON HF 665 is a highly alloyed with Cr-Mo-Nb-V-W hardfacing electrode. Special alloy addition gives microstructure of primary chromium carbide and complex carbide of Mo-Nb-V and W, so that the weld deposit can sustain severe abrasion and erosion resistance even at high temperature upto 6500C. Smooth and stable arc. Very High recovery with less slag.
Applications:
It is suitable for Coal burner pipes, Fibrizer/Mincer hammers, Sinter breaker arms, Hot Slag Conveyors, Clinker Conveyor chains, Augers, Slurry pumps, Billet Conveyor Guides, Coke pusher shoes, vertical Coal mill rollers etc. Also in mineral dressing equipments, specially where live coal and slag are treated.
Note on Usage:
Before welding remove oil and grease. Clean weld area by gouging or grinding to remove cracks or worn fatigued surface of components. Use electrode on AC/DC+ at the lowest amps. Electrode can be weaved 1.5 to 2 times its diameter. Peen deposits while hot. High carbon steel base metal to be preheated to 2500C. For higher build up on carbon or high alloy steels use SS 312 as a cushioning layer. For manganese steels, restrict heat build up to 1500C and use SAITRON 205 / SAITRON HF 600 WH alloy if necessary as a cushion layer. No preheat should be used on manganese steel.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 62 – 67 HRC |
| Diameter (mm) | 3.15 | 4.0 | 5.0 |
| Current (Amps) | 95-125 | 130-165 | 160-200 |
SAITRON SUGARARC
Description:
SAITRON SUGARARC is a specially developed for Surface Roughening of Sugar mill rolls. It is a high recovery electrode and gives eutectic of austenite and carbide weld deposits which can withstand abrasive conditions. Good corrosion resistance under wet condition. Achieved hardness approx. 550 BHN and retains upto 4000C. Weld droplets provides excellent gripping property. Increases Roller Life & crushing efficiency.
Applications:
SAITRON SUGAR-ARC is best for Surface Roughening of cast iron rolls in sugar industry. Gets good arcing in wet and dry condition. Helps in increasing the productivity.
Note on Usage:
Before welding remove oil and grease. Clean weld. Use electrode on AC/DC+ at the lowest amps. Hold the electrode according to Roller speed to achieve the desired weld droplets.
Typical Mechanical Properties of Weld Metal
| Hardness (As welded) | 58 – 62 HRC |
| Diameter (mm) | Length (mm) | Current (Amps) |
| 4.0 | 350 | 180 – 210 |